ANALISIS KEKUATAN TARIK KOMPOSIT PET (Polyethylene Terephthalate) DENGAN FRAKSI VOLUME MENGGUNAKAN RESIN EPOKSI DAN SERAT KELAPA SAWIT

Tiara Dewi Nabilah Farihah, . (2023) ANALISIS KEKUATAN TARIK KOMPOSIT PET (Polyethylene Terephthalate) DENGAN FRAKSI VOLUME MENGGUNAKAN RESIN EPOKSI DAN SERAT KELAPA SAWIT. Skripsi thesis, Universitas Pembangunan Nasional Veteran Jakarta.

[img] Text
ABSTRAK.pdf
Download (531kB)
[img] Text
AWAL.pdf
Download (2MB)
[img] Text
BAB 1.pdf
Download (1MB)
[img] Text
BAB 2.pdf
Restricted to Repository UPNVJ Only
Download (3MB)
[img] Text
BAB 3.pdf
Restricted to Repository UPNVJ Only
Download (1MB)
[img] Text
BAB 4.pdf
Restricted to Repository UPNVJ Only
Download (4MB)
[img] Text
BAB 5.pdf
Download (510kB)
[img] Text
DAFTAR PUSTAKA.pdf
Download (1MB)
[img] Text
RIWAYAT HIDUP.pdf
Restricted to Repository UPNVJ Only
Download (128kB)
[img] Text
LAMPIRAN.pdf
Restricted to Repository UPNVJ Only
Download (739kB)
[img] Text
HASIL PLAGIARISME.pdf
Restricted to Repository staff only
Download (589kB)
[img] Text
ARTIKEL KI.pdf
Restricted to Repository staff only
Download (681kB)

Abstract

Currently, rapid changes are taking place, and everyone is striving to develop technology and products to remain relevant with the times. This study aims to utilize coconut fiber waste and PET (Polyethylene Terephthalate) in the production of composites as a waste reduction measure. Variations in the volume fraction of palm fibers in PET composites were used to determine their influence on mechanical strength, with volume fractions of 10%:90%, 20%:80%, and 30%:70%. Tensile tests were conducted according to ASTM D638 standards using the hand lay-up and vacuum methods. Based on the research data, results for tensile strength and maximum elasticity modulus were obtained. From the obtained results, it was found that the best method was the vacuum method with a 30%:70% variation, where the distribution of the composite in the sample tended to be uniform. This was evidenced by the maximum values of tensile stress and elasticity modulus, which were relatively centered and displayed a uniform curve. The vacuum method yielded a tensile strength value of 9.75464 MPa and an elasticity modulus value of 49.21222 MPa.

Item Type: Thesis (Skripsi)
Additional Information: No. panggil:1910311012] [Pembimbing 1: Budhi Marthana] [Pembimning 2: Sigit Pradana] [Penguji 1: Fitri Wahyuni] [Penguji 2: James Julian]
Uncontrolled Keywords: Keyword: Plastic, Coconut fiber, Composite, Epoxy Resin, Tensile Test Value
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik > Program Studi Teknik Mesin (S1)
Depositing User: Tiara Dewi Nabilah Farihah
Date Deposited: 08 Aug 2023 08:49
Last Modified: 08 Aug 2023 08:49
URI: http://repository.upnvj.ac.id/id/eprint/25729

Actions (login required)

View Item View Item