Randy Firmansyah, . (2022) UJI KEKUATAN LASAN FRICTION STIR SPOT WELDING DIBAWAH PEMBEBANAN GESER TARIK PADA PADUAN ALUMINIUM. Skripsi thesis, Universitas Pembangunan Nasional Veteran Jakarta.
![[img]](http://repository.upnvj.ac.id/style/images/fileicons/text.png) |
Text
ABSTRAK.pdf Download (188kB) |
|
Text
Awalan.pdf Download (841kB) |
|
Text
BAB 1.pdf Download (326kB) |
|
Text
BAB 2.pdf Restricted to Repository UPNVJ Only Download (340kB) |
|
Text
BAB 3.pdf Restricted to Repository UPNVJ Only Download (721kB) |
|
Text
BAB 4.pdf Restricted to Repository UPNVJ Only Download (423kB) |
|
Text
BAB 5.pdf Download (299kB) |
|
Text
DAFTAR PUSTAKA.pdf Download (299kB) |
|
Text
RIWAYAT HIDUP.pdf Restricted to Repository UPNVJ Only Download (18kB) |
|
Text
LAMPIRAN.pdf Restricted to Repository UPNVJ Only Download (1MB) |
|
Text
HASIL PLAGIARISME.pdf Restricted to Repository staff only Download (9MB) |
|
Text
ARTIKEL KI.pdf Restricted to Repository staff only Download (263kB) |
Abstract
Technological advances in the emerging manufacturing sector are inseparable from welding as it plays an important role in metal fabrication and repair. Over the years improvements to increase productivity related to aluminum alloys in the manufacturing industry, has been widely researched and expanded. Problems in manufacturing today require fast and accurate processes to improve product quality in line with the spirit of the Industrial Revolution 4.0. In this study, aluminum sheet 1100 1 mm thick was welded using friction stir spot welding (FSSW) method and tested through tensile shear load test to determine the strength characteristics of the friction stir spot welding Weld results and also the influence on the combination of parameters such as spindle speed, tool depth, and residence time to the tensile shear load at the connection. The results showed that in each series of parameter combinations showed an attractive influence on tensile shear loads. The effect of 1400 rpm spindle speed showed good properties with the highest value of 71 MPa, especially at a tool depth of 0.6 mm. Furthermore, the influence of the tool depth has a significant effect on the tensile shear load, especially at 0.6 mm for each set of spindle speed and residence time. Each set of dwell time to the combination of parameters has no significant effect on the tensile shear load. Good tensile shear loads can be achieved in the range of 63-71 MPa at a tool depth of 0.6 mm and a spindle speed of 1400 rpm, where the best is 71 MPa at a standstill time of 9 seconds.
| Item Type: | Thesis (Skripsi) |
|---|---|
| Additional Information: | [No. Panggil: 1810311009] [Pembimbing: Armansyah} [Penguji 1: Sugeng Prayitno] [Penguji 2: James Julian] |
| Uncontrolled Keywords: | Keywords: Friction Stir Spot Welding, Tensile Shear Load Testing, Aluminium 1100 |
| Subjects: | T Technology > T Technology (General) T Technology > TJ Mechanical engineering and machinery T Technology > TS Manufactures |
| Divisions: | Fakultas Teknik > Program Studi Teknik Mesin (S1) |
| Depositing User: | RANDY FIRMANSYAH |
| Date Deposited: | 04 Mar 2023 02:47 |
| Last Modified: | 29 Nov 2024 12:20 |
| URI: | http://repository.upnvj.ac.id/id/eprint/21864 |
Actions (login required)
 |
View Item |