Hiezya Maryasha Abimanyu, . (2023) KARAKTERISTIK ORIENTASI SERAT PENGUAT MATERIAL COMPOSITE BERBAHAN CARBON FIBER DAN RESIN VINYL ESTER. Skripsi thesis, Universitas Pembangunan Nasional Veteran Jakarta.
![[img]](http://repository.upnvj.ac.id/style/images/fileicons/text.png) |
Text
ABSTRAK.pdf Download (190kB) |
|
Text
AWAL.pdf Download (1MB) |
|
Text
BAB 1.pdf Download (141kB) |
|
Text
BAB 2.pdf Restricted to Repository UPNVJ Only Download (725kB) |
|
Text
BAB 3.pdf Restricted to Repository UPNVJ Only Download (585kB) |
|
Text
BAB 4.pdf Restricted to Repository UPNVJ Only Download (1MB) |
|
Text
BAB 5.pdf Download (131kB) |
|
Text
DAFTAR PUSTAKA.pdf Download (135kB) |
|
Text
RIWAYAT HIDUP.pdf Restricted to Repository UPNVJ Only Download (148kB) |
|
Text
LAMPIRAN.pdf Restricted to Repository UPNVJ Only Download (9MB) |
|
Text
HASIL PLAGIARISME.pdf Restricted to Repository staff only Download (9MB) |
|
Text
ARTIKEL KI.pdf Restricted to Repository staff only Download (970kB) |
Abstract
Composites are materials composed of two or more different materials combined together to create a new material. Carbon fiber is often used as a reinforcing fiber in composite manufacturing due to its strong and lightweight properties. Carbon fiber materials, particularly unidirectional carbon, have variable fiber orientations that can be utilized in composite fabrication. This research aims to test carbon fiber composites with vinyl ester resin, using different fiber orientations of 0°, 45°, and a combination of 0° and 45°. Two different tests were conducted, namely tensile testing following ASTM D3039 standard and compression testing following ASTM D6641 standard. The results showed that the 0° fiber orientation exhibited the most optimal values compared to the other variables in both tests conducted. In the tensile test, the maximum tensile stress and maximum load obtained were 921 MPa and 14,105 N, respectively. For the compression test, the maximum compressive stress and maximum load were found to be 359 MPa and 9,550 N.
| Item Type: | Thesis (Skripsi) |
|---|---|
| Additional Information: | [No. Panggil : 19110311046] [Pembimbing 1 : Armansyah] [Pembimbing 2 : Budhi Martana] [Penguji 1 : Sugeng Prayitno] [Penguji 2 : Muchamad Oktaviandri] |
| Uncontrolled Keywords: | Composite, Carbon Fiber Orientation, Tensile Stress, Compressive Stress |
| Subjects: | T Technology > TJ Mechanical engineering and machinery T Technology > TP Chemical technology T Technology > TS Manufactures |
| Divisions: | Fakultas Teknik > Program Studi Teknik Mesin (S1) |
| Depositing User: | Hiezya Maryasha Abimanyu |
| Date Deposited: | 09 Aug 2023 05:53 |
| Last Modified: | 22 Aug 2023 03:24 |
| URI: | http://repository.upnvj.ac.id/id/eprint/25279 |
Actions (login required)
 |
View Item |